Add to ORKGThe curves obtained were used to evaluate the temperature at which maximum nucleation occurs, the activation energy of crystal growth and the crystallization mechanism. Comparison were made with the devitrification behaviour of a Na2O.2SiO2 glas
The non-isothermal devitrification of Na2O · 2 SiO2 glass prepared by gel-glass transformation is in...
The devitrification behaviour of specimens with compositions (2−x)Na2O(1+x)CaO·3 SiO2, O≤x≤ 1, was s...
The temp. of max. nucleation rate, the activation energy for crystal growth, and the reaction mechan...
The curves obtained were used to evaluate the temperature at which maximum nucleation occurs, the ac...
The non-isothermal devitrification of Na2O · 2 CaO · 3 SiO2 glass has been studied by differential t...
The non-isothermal devitrification of Na2O·2 SiO2 glass is investigated by differential thermal anal...
DTA and DDTA measurements have been used. For more than 70 mol% Sodium disilicate surface crystalliz...
The nucleation and crystallization of the Na2O · 2CaO · 3SiO2 (NC2S3) glass were studied by differen...
The effect of an increasing content of SiO2 in ternary glasses of compn. Na2O.CaO.xSiO2, where x = 2...
DTA at ≤590° was used to study nucleation and crystal growth in a 2Na2O.CaO.3SiO2 glass prepd. by me...
The nucleation rate (I) versus temperature type of curves for a Na 2O·2CaO·3SiO 2 (NC 2S 3) glass do...
The crystal nucleation of Li2O-2SiO2 glass is studied by DTA. A simple method based on the shift of ...
The non-isothermal devitrification of Na2O · 2 SiO2 glass prepared by gel-glass transformation is in...
The devitrification behaviour of specimens with compositions (2−x)Na2O(1+x)CaO·3 SiO2, O≤x≤ 1, was s...
The temp. of max. nucleation rate, the activation energy for crystal growth, and the reaction mechan...
The curves obtained were used to evaluate the temperature at which maximum nucleation occurs, the ac...
The non-isothermal devitrification of Na2O · 2 CaO · 3 SiO2 glass has been studied by differential t...
The non-isothermal devitrification of Na2O·2 SiO2 glass is investigated by differential thermal anal...
DTA and DDTA measurements have been used. For more than 70 mol% Sodium disilicate surface crystalliz...
The nucleation and crystallization of the Na2O · 2CaO · 3SiO2 (NC2S3) glass were studied by differen...
The effect of an increasing content of SiO2 in ternary glasses of compn. Na2O.CaO.xSiO2, where x = 2...
DTA at ≤590° was used to study nucleation and crystal growth in a 2Na2O.CaO.3SiO2 glass prepd. by me...
The nucleation rate (I) versus temperature type of curves for a Na 2O·2CaO·3SiO 2 (NC 2S 3) glass do...
The crystal nucleation of Li2O-2SiO2 glass is studied by DTA. A simple method based on the shift of ...
The non-isothermal devitrification of Na2O · 2 SiO2 glass prepared by gel-glass transformation is in...
The devitrification behaviour of specimens with compositions (2−x)Na2O(1+x)CaO·3 SiO2, O≤x≤ 1, was s...
The temp. of max. nucleation rate, the activation energy for crystal growth, and the reaction mechan...